Steel 20; quality, characteristics, range, scope of application and operating conditions

The alloy, which is characterized by ease of use, ease of processing, good strength and hardness, as well as low cost, can confidently be called universal, applicable in any conditions. Steel 20 is not a specialized steel; on the contrary, its application possibilities are so wide that it has found a place in almost every industrial sector.

Detailed information on the supply of sheet steel and a price calculator can be found on our website.

Total information

Steel 20 is a structural carbon quality steel widely used in industry. Its popularity is not inferior to 09G2S steel, although in terms of technical and operational characteristics there is a noticeable difference between these grades. Steel 20 is used mainly for the production of parts, welded structures, in construction, and mechanical engineering, but a complete list of industries for its use would take several pages of text. The practicality of steel of this grade allows it to occupy one of the leading positions on the market among ferrous rolled metals.

Characteristics

The metal is characterized by excellent weldability; there are no special requirements for welding, except in cases where the parts have previously been subjected to chemical or heat treatment. Steel 20 is not prone to temper brittleness and is insensitive to flakes and flake sensitivity. The alloy is resistant to pressure treatment, can be cut well by any means, does not crack, and is amenable to surface machining.

Steel 20 is less resistant to chemical attack; contact with alkalis and acids is not recommended. There is no protection against corrosion; products made from steel 20 are not recommended for use in conditions of high humidity, in contact with water without additional protective coatings (zinc, chrome or paint).

Heat treatment of steel 40Х

Heat treatment of steel 40X - alloy structural steel is intended for high-strength parts such as axles, shafts, gear shafts, plungers, rods, crank and cam shafts, rings, spindles, mandrels, racks, sponge rings, bolts, axle shafts, bushings and other parts increased strength. 40X steel is also often used to produce forgings, stampings and pipe fittings. However, the last listed parts require additional heat treatment, which consists of quenching through water in oil or simply in oil, followed by tempering in oil or air.

Decoding steel grade 40X. The number 40 indicates that the steel contains 0.4% carbon. Chromium content is less than 1.5%. In addition to the usual impurities, it contains specially introduced elements in certain quantities, which are designed to provide specially specified properties. In this case, chromium is used as an alloying element, as indicated by the corresponding marking.

Heat treatment of steel 20

Heat treatment of steel 20 - high-quality structural carbon steel. Widely used in boiler making, for pipes and heating pipelines for various purposes; in addition, the industry produces rods and sheets. The starting temperature for forging steel 20 is 1280° C, the end temperature is 750° C, the forging is cooled by air. Steel 20 is non-flock sensitive and not prone to tempering. After carburization and cyanidation, steel 20 can be used to produce parts that require high surface hardness and can tolerate low core strength: cam rollers, fasteners, spindles, sprockets, studs, link forks and shift shafts gears, valve tappets, oil pump rollers. Steel 20 is used for the production of lightly loaded parts (pins, axles, copiers, stops, gears), cemented parts for long and very long service (operation at temperatures not exceeding 350 ° C), thin parts exposed to abrasion and other parts of automotive and agricultural mechanical engineering.

Heat treatment of steel 30khgsa

Heat treatment of steel 30xgsa - refers to medium-alloy structural steel. Steel 30xgsa undergoes improvement - hardening followed by high tempering at 550-600 ° C, therefore it is used in the creation of improved parts (except for aircraft parts, these can be various casings, axles and shafts, blades of compressor machines that operate at 400 ° C, and much more), levers, pushers, critical welded structures operating under alternating loads, fasteners operating at low temperatures. Steel 30xgsa has good endurance, excellent impact strength, and high strength. It also has excellent weldability.

Welding 30xgsa steel also has its own characteristics. It is carried out with preheating of the material to 250-300 ° C, followed by slow cooling. This procedure is very important because cracks may appear due to the sensitivity of the steel to sudden temperature changes after welding. Therefore, upon completion of welding work, the torch should be withdrawn slowly, while heating the material at a distance of 20-40 mm from the welding site. Also, no more than 8 hours after completion of welding, welded joints of 30KhGSA steel require quenching with heating to 880 °C, followed by high tempering. Next, the product is cooled in oil at 20-50 °C. Tempering is carried out by heating to 400 - 600 ° C and cooling in hot water. Welding must be performed as quickly as possible in order to avoid burnout of alloying elements. After undergoing thermomechanical low-temperature treatment, 30KhGSA steel acquires a tensile strength of up to 2800 MPa, impact strength doubles (in contrast to conventional heat treatment of 30KhGSA steel), and ductility increases.

Heat treatment of steel 65g

Heat treatment of steel 65g - Structural spring steel. Springs, leaf springs, thrust washers, brake bands, friction discs, gears, flanges, bearing housings, clamping and feed collets and other parts that require increased wear resistance and parts that operate without shock loads are used in industry. (substitutes: 70, U8A, 70G, 60S2A, 9HS, 50HFA, 60S2, 55S2).

Heat treatment of steel 40 - High-quality carbon structural steel. Industrial use: pipes, forgings, fasteners, shafts, discs, rotors, flanges, gears, bushings for long and very long service at temperatures up to 425 degrees.

Heat treatment of steel 40xn - Structural alloy steel Use in industry: axles, shafts, connecting rods, gears, excavator shafts, couplings, gear shafts, spindles, bolts, levers, rods, cylinders and other critical loaded parts subject to vibration and dynamic loads , which are subject to requirements for increased strength and toughness. Rolls of rail and beam and large-section mills for hot rolling of metal.

Heat treatment of steel 35 - High-quality carbon structural steel. Use in industry: parts of low strength that experience low stress: axles, cylinders, crankshafts, connecting rods, spindles, sprockets, rods, rims, traverses, shafts, tires, discs and other parts.

Heat treatment of steel 20Х13 - Corrosion-resistant, heat-resistant steel. Use in industry: power engineering and furnace making; turbine blades, bolts, nuts, fittings for cracking units with a long service life at temperatures up to 500 degrees; martensitic class steel Steel grade 20Х13 and other martensitic class steels: heat-resistant martensitic chromium steels are used in various power plants; they operate at temperatures up to 600° C. Rotors, disks and turbine blades are made from them, and recently they have been used for ring parts large thicknesses. There are a large number of steel grades of this class. Common to all is a reduced chromium content, the presence of molybdenum, vanadium and tungsten. They are effectively strengthened by conventional heat treatment methods, which are based on the y-a transformation and provide for the formation of martensite in the structure with subsequent improvement depending on the technical requirements. (substitutes: 12Х13, 14Х17Н2)

Advantages and disadvantages of steel 20

Steel 20 is distinguished by its quality and relatively low production cost. It is an upgradeable alloy, making it adaptable to a wide range of conditions and, as a result, widespread.

Steel 20 is corrosion-resistant and susceptible to chemical influences - this is its main drawback. The advantages include:

• good weldability without special requirements for the procedure;
• disinclination to temper fragility;
• insensitivity to flakes;
• price-quality ratio;
• material density;
• moderate strength.

Steel 20 is a ferrous metal with a simple composition without expensive alloying additives. The alloy has been produced for a long time, the production process is well studied, optimized, and worked out; There are no special conditions or requirements, so the metal is not very expensive.

Letter designations of steels and their interpretation

The chemical composition of many alloyed structural steels is determined by GOST 4543–71 “Rolled products from alloyed structural steel. Technical conditions". The same standard defines the basic letter symbols for designating alloying elements. It must be taken into account that steels are currently produced with additions of elements, the designation of which is not provided for by the standard. In this case, the elements in the steel grade are usually designated by the first letters of the name.

Read also: Connecting a com port to the motherboard

The symbolic letter designations of the main alloying elements are given below.

Steel grades

is a classification of steels according to their chemical composition and physical properties. In Russia, the USA [1], Europe [2], Japan [3] and China [4], various marking methods are used for similar steels.

Explanation of markings

The marking of steel 20 indicates the chemical composition of the alloy, in particular; on the proportion of carbon in the composition. Since 20 steel is considered high quality, higher demands are placed on the accuracy of its chemical composition.

Chemical composition

The chemical composition of steel 20 includes the following elements and their designations:

• Carbon. The first digit 20 indicates the carbon content in hundredths, i.e. 0.2%. The advantage of steel with a high carbon content is higher strength, but this same indicator leads to a decrease in ductility.
• Silicon. The proportion of silicon in the alloy ranges from 0.17 to 0.35%. Due to the presence of silicon in the metal composition, porosity and the number of gas pockets, which negatively affect the strength of the alloy, are reduced. Pores and cavities are formed due to oxygen, nitrogen and hydrogen gases, the particles of which are removed by silicon.
• Manganese. The proportion of manganese ranges from 0.35 to 0.6%. Manganese, like silicon, prevents oxidation and also removes sulfur from the composition. Thanks to manganese, heat treatment under pressure occurs with a low probability of crack formation, the effectiveness of forging and welding works improves, and the surface of products becomes of higher quality.
• Chrome, copper, nickel. The proportion of nickel and copper usually does not exceed 0.3%, the proportion of chromium; 0.2%. These are alloying additives that have a positive effect on the properties of steel, but in this case their content is insignificant, so they do not have a noticeable effect on the characteristics of the alloy.
• Phosphorus, sulfur. Phosphorus content is permissible up to 0.035%, sulfur; up to 0.04%. These are impurities that have a harmful effect on steel. They increase brittleness and negatively affect toughness, as a result of which the steel loses its resistance to dynamic loads.
• Iron. The rest of the alloy is iron.

Chemical composition in % of material 20

GOST 1050-88

Chemical composition

Fe is the basis. According to TU 14-1-1672-76, the chemical composition is given for steel grade 20A. The residual copper content is allowed no more than 0.25% when steel is smelted using the scrap process. Deviations from the norms of chemical composition are allowed in accordance with GOST 1050. Upon request, steel can be supplied with narrowed carbon content limits - “select”: 0.19-0.25%; 0.19-0.23%; 0.22-0.25%; 0.21-0.24%. According to GOST 1050-88, the nitrogen content is indicated for steel using the oxygen-converter smelting method. For all other types of steelmaking, the nitrogen content is N≤0.008%. According to TU 14-1-5185-93, TU 14-1-5058-91, the chemical composition is given for steel grade 20pv. According to TU 08.002.0501.5348-92, the chemical composition is given for steel grade 20-Sh. According to TU 14-1-3987-85, the chemical composition is given for steel grade 20. According to TU 14-1-1529-2003, TU 14-3-460-2003 and TU 14-3-341-75 for steel made from scrap process or from cuprous ores, the mass fraction of residual copper and nickel is allowed up to 0.30% each. The technological addition of rare earth elements is allowed to improve the quality of the metal. According to TU 14-3R-55-2001, the chemical composition is given for steel 20; for steel 20-PV, the mass fraction of carbon is 0.18-0.24%, chromium, nickel, copper, sulfur and phosphorus ≤ 0.15% each, the mass fraction of other elements is identical to steel grade 20. In steel 20, nickel and chromium no more than 0.40% each. The presence of rare earth elements introduced as technological additives is allowed. According to GOST 19277-73, GOST 21729-76, the chemical composition is given for steel 20A. When smelting steel using the scap process, the mass fraction of copper should be ≤ 0.25%. Maximum deviations for the chemical composition are in accordance with GOST 1050. According to TU 1317-006.1-593377520-2003, the chemical composition is given for steel grade 20A. The mass fraction of hydrogen in steel in the pipe metal should not exceed 1.0 ppm (2.0 ppm in the ladle sample. It is allowed to introduce niobium and titanium to obtain a mass fraction of up to 0.030% and 0.010%, respectively. In deoxidized steel for globularization of sulfide inclusions calcium (silicocalcium) or cerium is introduced to obtain a mass fraction of 0.050%. According to TU 14-162-14-96, the chemical composition is given for steel grade 20A. Deviations in the content of carbon (-0.020%), aluminum (±0.010%) are allowed in steel ), manganese (+0.15%), sulfur (+0.005%), phosphorus (+0.005%). In order to increase strength properties, it is allowed to introduce vanadium into steel in an amount of up to 0.050%. According to TU 14-3-1971-97 The chemical composition is given for steel grade 20B with increased corrosion resistance and operational reliability. To ensure a fine-grained structure, vanadium is introduced up to 0.06%. The carbon equivalent SEq should not exceed 0.40%. According to TU 1301-039-00212179-2010, the chemical composition is given for steel grade 20-Sh. The content of each impurity element not regulated by the table is allowed up to 0.050%. According to TU 108.1273-84, deviations for nickel are +0.20%, for copper +0.20%. According to TU 14-158-113-99, the chemical composition is given for steel grade 20 with increased corrosion resistance and cold resistance. In the finished metal, deviations in chemical composition are allowed in accordance with GOST 1050, in addition - for aluminum + 0.0050%. When the mass fraction of nitrogen is more than 0.0080%, microalloying with vanadium of at least 0.030% is mandatory. According to TU 14-161-149-94, the chemical composition is given for steel grade 20 for hydrogen sulfide- and cold-resistant casing pipes and couplings.

Types of rental

There are two main technologies for producing rolled profiles from steel 20:

1. Hot deformation - used for rolling workpieces more than 4 mm thick. Hot deformation leads to the formation of scale, which is the main disadvantage of this technology.
2. Cold deformation; used for rolling thin workpieces (up to 4 mm). As a result of cold deformation, the strength of the alloy increases due to cold hardening.

Types of steel products 20

• profile of all varieties: channel, sheet, I-beam, angle, rod, wire;
• seamless, high-strength pipes obtained by drawing (cold or hot);
• all-welded cold-rolled pipes, welded from a single sheet of steel 20 along the length of the pipe.

Production Standards

• long products, including shaped steel - GOST 1050-88, GOST 2590-2006, GOST 2591-2006, GOST 2879-2006, GOST 8509-93, GOST 8510-86, GOST 8240-97, GOST 8239-89;
• calibrated rod - GOST 7417-75, GOST 8559-75, GOST 8560-78, GOST 10702-78;
• polished rod and silver - GOST 14955-77;
• thick sheet - GOST 1577-93, GOST 19903-74;
• thin sheet - GOST 16523-97;
• tape - GOST 6009-74, GOST 10234-77, GOST 103-2006, GOST 82-70;
• wire - GOST 5663-79, GOST 17305-91;
• forgings and forged blanks - GOST 8479-70;
• pipes - GOST 10704-91, GOST 10705-80, GOST 8731-74, GOST 8732-78, GOST 8733-74, GOST 5654-76, GOST 550-75.

Purpose and application

Steel 20 is one of the most common steel grades in the domestic industry; its versatility allows the production of almost all types of metal products. The main areas of application of steel 20:

1. Mechanical engineering. Steel 20 is used to make fastening devices, connecting elements of mechanisms, gears, worms, brackets, bearing shafts, and liners.
2. Pipelines. Steel 20 is used to make welded and seamless pipes, shut-off valves and adapters; crosspieces, union nuts, nipples, fittings, hexagons, couplings, taps, manifolds, superheaters, parts of boilers operating under high pressure.
3. Construction. Fasteners, hooks, load-bearing trusses, beams and much more. In construction, steel 20 is popular due to its good weldability, satisfactory strength and availability.

Structural quality carbon steel 20

Structural high-quality carbon steel is used for the production of hot-rolled sheets, circles, strips, seamless pipes, electric-welded pipes, hexagons, manifolds, pipelines, superheaters, other parts of high-pressure boilers, sheets for stamping, cemented products with a long service life at temperatures up to +3500C.

Steel 20 is one of the most practical steel grades, widely used for the production of steel pipes and hot-rolled sheets.

Metal grade Substitute

Three types of steel 20 according to deoxidation level

Deoxidation is the removal of oxygen from the composition of steel 20 in order to reduce the brittleness during hot working. The degree or level of deoxidation can also be called the degree of gas evolution during steel solidification. The intensity of gas evolution or boiling greatly affects the structure of the frozen metal; accordingly, the higher the level of deoxidation, the more solid and durable the structure will be.

Quiet and semi-quiet steel

Steel, which is deoxidized by silicon and manganese, can be maximally purified of oxygen content. Such steel is characterized by a complete structure without bubbles and pores, because the alloy solidifies in a calm state, without active release of gases. The formation of a shrinkage cavity occurs in the upper part; it is removed mechanically.

Quiet steel is more expensive than boiling and semi-quiet steel, because more difficult to produce. It is used in the manufacture of products with high strength requirements, for example, for load-bearing structures, railway tracks, etc.

Semi-quiet steel; an average state between calm and boiling steel, characterized by medium porosity. It comes in different qualities and is used for the manufacture of welded structures, blanks for rolled pipes, and fasteners.

Calm steel has the highest levels of strength and reliability, but its use may not be economically viable in industries where high demands are not placed on steel products.

Boiling steel

Steel 20, the deoxidation process of which is carried out thanks to manganese, contains the largest amount of dissolved gases and iron oxides. When boiling steel hardens, nitrogen and carbon dioxide are actively released, and multiple bubbles and pores are formed. Such steel is inferior to calm and semi-quiet steel in terms of strength, but has a number of positive characteristics. It is perfectly stamped, the process of its production is simpler and cheaper, and the production is waste-free.

Boiling steel is suitable for the production of products that are not subject to high loads during operation. This can be various types of fencing, sheet cladding, and other metal structures.

Carbon steel of ordinary quality

Carbon steels are divided into three main groups : carbon steels of ordinary quality, high-quality carbon steels and carbon steels for special purposes (automatic steel, boiler room, etc.).
Carbon steels of ordinary quality comply with GOST 380–2005. They are supplied in the form of rolled products in a normalized condition and are used in mechanical engineering, construction and other sectors of the national economy.

Carbon steels of ordinary quality are designated by the letters St and numbers from 0 to 6.

The numbers are the conditional number of the brand. The higher the number, the higher the carbon content, higher the strength and lower the ductility.

Depending on the purpose and guaranteed properties, carbon steels of ordinary quality are supplied in three groups : A, B, C. The indices to the right of the grade number mean:

1. kp - boiling;
2. ps - semi-calm;
3. sp - calm.

The letter G may appear between the index and the brand number; this means a high manganese content. The grade designations to the left of the letters St indicate the groups (B and C) of steel. Ordinary quality steels are divided into categories . The steel category is indicated by the corresponding number to the right of the deoxidation degree index. For example, St5Gps3 means: steel of group A, grade St5, with a high manganese content, semi-calm, third category. Steel of the first category is written without indicating the number of the last, for example St4ps.

The chemical composition of group A steels is not regulated, but their mechanical properties are guaranteed, determined by the relevant state standard. Steels of this group are usually used for parts that are not subjected to hot processing (welding, forging, etc.) during the manufacturing process.

Group B steel is supplied according to its chemical composition and is used for parts that undergo heat treatment and hot pressure treatment (stamping, forging) during the manufacturing process. The mechanical properties of group B steel are not guaranteed. Group B steel is supplied with mechanical properties corresponding to the standards for group A steel, and a chemical composition corresponding to the standards for group B steel. Group B steel is used mainly for welded structures.

Mechanical properties

Steel 20 is characterized by high mechanical properties, such as ductility, hardness and strength. The high impact strength allows the steel to adequately withstand increased dynamic loads. Strength is improved by thermal or mechanical treatments - peening, roller rolling, annealing, normalization.

The specific gravity of steel is 7.85 g/cm3. Maximum linear expansion coefficient st 20 = 14.8·10-6 deg-1 at temperatures 27-700°C. Indicators for calibrated hot-rolled steel of the 2nd category: temporary tensile strength 410 MPa, relative elongation after fracture 25%, relative contraction 55%, Brinell hardness 4.8.

Mechanical properties at T=20oC of the material 20.

Mechanical properties of steel 20 at elevated temperatures 0С

Steel endurance limits 20

Mechanical properties of steel 20 after chemical treatment

Designations used in tables

Mechanical properties:

• sв — Short-term strength limit, [MPa]
• sT — Yield strength, [MPa]
• s0.2 - Limit of proportionality (permanent deformation tolerance - 0.2%), [MPa]
• d5 — Elongation at break, [%]
• y — Relative narrowing, [%]
• KCU - Impact strength, [kJ/m2]
• HB - Brinell hardness, [MPa]
• HV — Vickers hardness, [MPa]
• HSh - Shore Hardness, [MPa]

Physical properties:

• T — Temperature at which these properties were obtained, [degrees]
• E — Modulus of elasticity of the first kind, [MPa]
• a - Coefficient of thermal (linear) expansion (range 20o - T), [1/degree]
• l — Thermal conductivity coefficient (heat capacity of the material), [W/(m deg)]
• r — Material density, [kg/m3]
• C - Specific heat capacity of the material (range 20o - T), [J/(kg deg)]
• R — Electrical resistivity, [Ohm m]

• Buy steel circles 20

Ferrous rolled metal Stainless steel rolled Pipeline elements Pipe fittings Non-ferrous rolled metal Fasteners and hardware Metal structures Corrugated sheeting Roofing materials Welding materials

Technological properties

Steel 20 is a high-tech alloy classified as cemented. The cementation process is the saturation of the surface of a product with carbon by heating in a special environment. As a result of this treatment, the top layer of the product acquires a hardness value of up to 62 HRC, which is three times higher than that of the core. The metal lends itself well to forging, cutting and soldering, is not prone to cracking, and retains high density. All popular methods are applicable for welding - ADS, KTS, RDS, submerged arc welding, etc. The type of equipment depends on the selected welding technology.

Impact strength of steel 20 KCU (J/cm3) at low temperatures °C

Steel yield strength 20

Hardness

Physical properties

The melting point of steel 20 is 1500C, steel becomes liquid at 1600C. Steel 20 has good thermal conductivity and heat capacity. The modulus of elasticity, coefficient of thermal expansion, thermal conductivity, density, specific heat capacity and electrical resistivity for various temperatures are shown in the table below.

Physical properties of the material 20 .

Foreign analogues and substitutes

The main domestic substitute for 20K steel, which is closest to it in terms of performance characteristics, is 15K steel. For information on foreign analogues, see the table below.